      treatment of steel by heat or mechanical means to increase the hardness of the outer surface while the core remains relatively soft. The combination of a hard surface and a soft interior is greatly valued in modern engineering because it can withstand very high stress and fatigue, a property that is required in such items as gears and anti-friction bearings. Surface-hardened steel is also valued for its low cost and superior flexibility in manufacturing.

      The oldest surface-hardening method is carburizing, in which steel is placed at a high temperature for several hours in a carbonaceous environment. The carbon diffuses into the surface of the steel, rendering it harder. Various techniques of carburizing have been developed to increase efficiency and reduce cost. The pack method involves packing into a steel box the parts to be hardened along with a compound of charcoal or coke to which carbonates have been added. The pack is then heated to a very high temperature, usually 1,700°–1,750° F (925°–955° C). The depth of the carbon penetration depends on the exposure time and temperature. In gas carburizing the parts are heated in contact with such carbon-bearing gases as carbon monoxide, carbon dioxide, methane, or propane. This process is usually done in a large furnace into which the parts are fed at one end and from which they emerge at the other end in the hardened state. The same process is used in carbonitriding except that ammonia is added to the furnace atmosphere and it takes place at lower temperatures that produce less distortion in the steel. Gears, ball and roller bearings, and piston pins are among the products made by carburizing.

      Another method of surface hardening, called nitriding, utilizes nitrogen and heat. Cam shafts, fuel injection pumps, and valve stems are typically hardened by this process. Flame hardening and induction hardening, in which high heat is applied for a short time (by gas flame or high-frequency electric current, respectively) and then the steel is immediately quenched, are used generally for larger implements.

      Mechanical means of hardening the surface of steel parts include peening, which is the hammering of the heated surface, as by iron pellets shot onto the surface or by air blasting, and cold-working, which consists of rolling, hammering, or drawing at temperatures that do not affect the composition of the steel.

* * *


Universalium. 2010.

Игры ⚽ Нужно решить контрольную?

Look at other dictionaries:

  • Surface hardening — Surface hardening. См. Поверхностное упрочнение. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) …   Словарь металлургических терминов

  • surface hardening — paviršinis grūdinimas statusas T sritis fizika atitikmenys: angl. flame hardening; surface hardening vok. Brennhärtung, f; Oberflächenhärtung, f rus. пламенная закалка, f; поверхностная закалка, f pranc. durcissement de la surface, m;… …   Fizikos terminų žodynas

  • surface hardening — a method of hardening the surface of steel to increase its wear resistance. Depending on the analysis of the steel, the following treatments can be employed: case hardening, nitriding, induction hardening, flame hardening …   Mechanics glossary

  • hardening — increasing the hardness of steel by heat treatment. This normally implies heating the steel to a required temperature and quenching in a suitable medium, e.g., oil or water. age hardening case hardening cyanide hardening flame hardening induction …   Mechanics glossary

  • Surface finishing — is a broad range of industrial processes that alter the surface of a manufactured item to achieve a certain property.[1] Finishing processes may be employed to: improve appearance, adhesion or wettability, solderability, corrosion resistance,… …   Wikipedia

  • Hardening — Hard en*ing, n. 1. Making hard or harder. [1913 Webster] 2. That which hardens, as a material used for converting the surface of iron into steel. [1913 Webster] …   The Collaborative International Dictionary of English

  • surface harden — transitive verb : to harden the surface of (as steel) by a case hardening process or other method (as induction or flame) …   Useful english dictionary

  • Case hardening — or surface hardening is the process of hardening the surface of a metal, often a low carbon steel, by infusing elements into the material s surface, forming a thin layer of a harder alloy. Case hardening is usually done after the part in question …   Wikipedia

  • Induction hardening — is a form of heat treatment in which a metal part is heated by induction heating and then quenched. The quenched metal undergoes a martensitic transformation, increasing the hardness and brittleness of the part. Induction hardening is used to… …   Wikipedia

  • Diffusion hardening — Schematic cutaway view of a diffusion hardened metal gear Diffusion hardening is a process used in manufacturing that increases the hardness of steels. In diffusion hardening, diffusion occurs between a steel with a low carbon content and a… …   Wikipedia

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”