nuclear ceramics


nuclear ceramics

Introduction

      ceramic materials employed in the generation of nuclear power (nuclear energy) and in the disposal of radioactive nuclear wastes.

      In their nuclear-related functions, ceramics are of major importance. Since the beginning of nuclear power generation, oxide ceramics, based on the fissionable metals uranium and plutonium, have been made into highly reliable fuel pellets for both water-cooled and liquid-metal-cooled reactors. Ceramics also can be employed to immobilize and store nuclear wastes. Although vitrification (glass formation) is a favoured approach for waste disposal, wastes can be processed with other ceramics into a synthetic rock, or synroc, or they can be mixed with cement powder to make hardened cements. All these nuclear applications are extremely demanding. In addition to severe thermal and chemical driving forces, nuclear ceramics are continuously subjected to high radiation doses.

      This article describes properties and applications of ceramics as nuclear fuels and as waste-disposal materials. For discussion of the employment of glassy and metallic materials in nuclear waste disposal, see materials science: Materials for energy (materials science). For the production of metallic uranium and plutonium and their conversion to oxide form, see uranium processing. For detailed description of nuclear reactors and the nuclear fuel cycle, see nuclear reactor.

Nuclear fuel
 Ceramic oxide fuels were introduced in the 1950s, following military applications of nuclear power. Urania (uranium dioxide, UO2) and plutonia (plutonium dioxide, PuO2) have unique features that qualify them for nuclear fuel applications. First, they are extremely refractory: for instance, the melting point of UO2 is in excess of 2,800° C (5,100° F). Second, the open crystal structure of oxide nuclear ceramics allows for retention of fission products, and their highly variable oxygen-to-metal ratio can shift to accommodate burnup. They therefore have excellent resistance to radiation damage. (The crystal structure of urania is illustrated in Figure 2B—> of the article ceramic composition and properties: Crystal structure (ceramic composition and properties).)

       Selected properties of ceramic nuclear fuelsOther advantages of oxide nuclear fuels include inertness to many coolants, long burnup without swelling, and relatively low fabrication cost. One drawback is low thermal conductivity. This has prompted research on replacing the oxides with more conductive carbides or nitrides. Selected properties of oxide, carbide, and nitride nuclear fuels are compared in Table 1 (Selected properties of ceramic nuclear fuels).

      The fabrication of ceramic nuclear fuels traditionally follows a standard powder-pellet process. This involves comminution, granulation, pressing, and sintering at 1,700° C (3,100° F) in a reducing atmosphere. The resulting microstructure consists of large, equiaxed grains (that is, with dimensions similar along all axes), with uniformly distributed spherical pores on the order of 2 to 5 micrometres (0.00008 to 0.0002 inch). The pores are intended to retain fission gas and to decrease swelling during burnup.

      Ceramic fuel pellets also can be fabricated in an advanced process called sol-gel microsphere pelletization. The sol-gel route (described in the article advanced ceramics) achieves homogeneous distribution of uranium and plutonium in solid solution, enables sintering to occur at lower temperature, and ameliorates the toxic dust problem associated with the powder-pellet method.

Nuclear waste disposal

High-level waste
      A 1,000-megawatt nuclear power reactor produces on the order of 20–25 tons of spent fuel per year. Spent fuel is initially stored for up to several decades underwater in storage pools. This allows the high-activity, short-half-life radioactivity to decay. Some of this material can be reprocessed to recover reusable uranium and plutonium. However, the waste also contains radioactive isotopes with much longer half-lives. It is widely accepted that this high-level waste (HLW) must be incorporated into a solid form prior to burial in deep geologic repositories.

      The requirements of a nuclear waste form for HLW are rigorous. The waste form must be able to take into solid solution or at least to encapsulate the radioactive species. This is necessary so that the rate of leaching into underground water in a geologic repository will be acceptably low. Leach resistance must be maintained against deterioration of the waste form by radiation damage over long time periods, possibly lasting thousands of years. The form must be amenable to fabrication into large cylindrical monoliths, approximately 30 centimetres (1 foot) in diameter, with minimal internal cracking. Other important considerations are low cost and personnel safety from such hazards as respirable dust and radiation exposure.

      In most nuclear countries the accepted first-generation solid form for disposing of HLW is borosilicate glass (Pyrex). In borosilicate forms, some radioactive species become part of the glass structure and others are merely encapsulated. The most advanced second-generation solid waste form is synroc, a ceramic synthetic rock. Synroc contains various titanate-mineral phases that have the capability of forming solid solutions with nearly all the radioactive species in HLW. Similar minerals exist in nature, where they have survived under demanding conditions for geologic time periods. The production of synroc involves mixing oxides or appropriate alkoxides with HLW, drying and calcining under reducing conditions, and hot-pressing or hot-isostatic-pressing the powder in graphite or refractory metal dies. (Hot pressing and hot isostatic pressing are described in the article advanced ceramics.)

Low-level waste
      Over the years low-level wastes (LLW) have accumulated from the processing of nuclear fuels and wastes. These consist of aqueous solutions and sludges, which customarily have been stored in steel-lined underground tanks. However, concerns over actual and potential leaks from these tanks leading to groundwater contamination have prompted the development of solid waste forms for LLW. Some of this material will be glassy, but one promising route is to make cement with the aqueous LLW. Immobilization of some radioactive species would take place by chemical incorporation into the cementitious product phases; the rest would be immobilized within the pores of the cement paste. Extremely low permeabilities (and therefore low leach rates) can be achieved in microstructurally engineered cements.

 Nuclear ceramics are only one type of advanced structural ceramic. For a survey of the issues involved in adapting ceramics for demanding structural applications, see advanced structural ceramics. For a directory to all the articles covering both traditional and advanced industrial ceramics, see Industrial Ceramics: Outline of Coverage—.

Additional Reading
Specific information on nuclear ceramics is provided by two articles in R.J. Brook, Robert W. Cahn, and Michael B. Bever (eds.), Concise Encyclopedia of Advanced Ceramic Material (1991): R.D. Leggett, “Oxide Nuclear Fuels,” pp. 337–40; and K.D. Reeve, “Nuclear Waste Storage Materials,” pp. 331–35. The section titled “Structural Applications for Technical, Engineering, and Advanced Ceramics,” in Theodore J. Reinhart (ed.), Engineered Materials Handbook, vol. 4, Ceramics and Glasses, ed. by Samuel J. Schneider (1991), pp. 959–1014, presents an overview of advanced structural ceramics.Thomas O. Mason

* * *


Universalium. 2010.

Look at other dictionaries:

  • advanced structural ceramics — Introduction       ceramic materials that demonstrate enhanced mechanical properties under demanding conditions. Because they serve as structural members, often being subjected to mechanical loading, they are given the name structural ceramics.… …   Universalium

  • industrial ceramics —       Ceramics are broadly defined as inorganic, nonmetallic materials that exhibit such useful properties as high strength and hardness, high melting temperatures, chemical inertness, and low thermal and electrical conductivity but that also… …   Universalium

  • Corium (nuclear reactor) — LFCM redirects here. For the airport, see List of airports by ICAO code: L. The Three Mile Island reactor 2 after the meltdown. Corium, also called fuel containing material (FCM) or lava like fuel containing material (LFCM), is a lava like molten …   Wikipedia

  • Institute of Nuclear and New Energy Technology — The Institute of Nuclear and New Energy Technology (INET ) of Tsinghua University, China was founded in 1960 as a top nuclear research and experimental base. It is located in the northern suburbs of Beijing near Changping tiger village. It is the …   Wikipedia

  • Business and Industry Review — ▪ 1999 Introduction Overview        Annual Average Rates of Growth of Manufacturing Output, 1980 97, Table Pattern of Output, 1994 97, Table Index Numbers of Production, Employment, and Productivity in Manufacturing Industries, Table (For Annual… …   Universalium

  • Industrial Review — ▪ 1994 Introduction       The period since 1990 was proving a difficult time for the older industrialized economies, which had suffered from prolonged recession at home, and also for the previously centrally planned economies of Eastern Europe… …   Universalium

  • materials science — the study of the characteristics and uses of various materials, as glass, plastics, and metals. [1960 65] * * * Study of the properties of solid materials and how those properties are determined by the material s composition and structure, both… …   Universalium

  • Anthropology and Archaeology — ▪ 2009 Introduction Anthropology       Among the key developments in 2008 in the field of physical anthropology was the discovery by a large interdisciplinary team of Spanish and American scientists in northern Spain of a partial mandible (lower… …   Universalium

  • technology, history of — Introduction       the development over time of systematic techniques for making and doing things. The term technology, a combination of the Greek technē, “art, craft,” with logos, “word, speech,” meant in Greece a discourse on the arts, both… …   Universalium

  • pre-Columbian civilizations — Introduction       the aboriginal American Indian (Mesoamerican Indian) cultures that evolved in Meso America (part of Mexico and Central America) and the Andean region (western South America) prior to Spanish exploration and conquest in the 16th …   Universalium


We are using cookies for the best presentation of our site. Continuing to use this site, you agree with this.