magnesium processing


      preparation of the ore for use in various products.

      Magnesium (Mg) is a silvery white metal that is similar in appearance to aluminum but weighs one-third less. With a density of only 1.738 grams per cubic centimetre, it is the lightest structural metal known. It has a hexagonal close-packed (hcp) crystalline structure, so that, like most metals of this structure, it lacks ductility when worked at lower temperatures. In addition, in its pure form, it lacks sufficient strength for most structural applications. However, the addition of alloying elements improves these properties to such an extent that both cast and wrought magnesium alloys are widely used, particularly where light weight and high strength are important.

      Magnesium is strongly reactive with oxygen at high temperatures; above 645° C (1,190° F) in dry air, it burns with a bright white light and intense heat. For this reason, magnesium powders are used in pyrotechnics. At room temperature, a stable film of water-insoluble magnesium hydroxide forms on the metal's surface, protecting it from corrosion in most atmospheres. Being a strong reactant that forms stable compounds with chlorine, oxygen, and sulfur, magnesium has several metallurgical applications, such as in the production of titanium from titanium tetrachloride and in the desulfurization of blast-furnace iron. Its chemical reactivity is also evident in the magnesium compounds that have wide application in industry, medicine, and agriculture.

      Magnesium derives its name from magnesite, a magnesium carbonate mineral, and this mineral in turn is said to owe its name to magnesite deposits found in Magnesia, a district in the ancient Greek region of Thessaly. The British chemist Humphry Davy (Davy, Sir Humphry, Baronet) is said to have produced an amalgam of magnesium in 1808 by electrolyzing moist magnesium sulfate, using mercury as a cathode. The first metallic magnesium, however, was produced in 1828 by the French scientist A.-A.-B. Bussy. His work involved the reduction of molten magnesium chloride by metallic potassium. In 1833 the English scientist Michael Faraday (Faraday, Michael) was the first to produce magnesium by the electrolysis of molten magnesium chloride. His experiments were repeated by the German chemist Robert Bunsen.

      The first successful industrial production was begun in Germany in 1886 by Aluminium und Magnesiumfabrik Hemelingen, based on the electrolysis of molten carnallite. Hemelingen later became part of the industrial complex IG Farbenindustrie, which, during the 1920s and '30s, developed a process for producing large quantities of molten and essentially water-free magnesium chloride (now known as the IG Farben process) as well as the technology for electrolyzing this product to magnesium metal and chlorine. Other contributions by IG Farben were the development of numerous cast and malleable alloys, refining and protective fluxes, wrought magnesium products, and a vast number of aircraft and automobile applications. During World War II the Dow Chemical Company of the United States and Magnesium Elektron Limited of the United Kingdom began the electrolytic reduction of magnesium from seawater pumped from Galveston Bay, Texas, and the North Sea at Hartlepool, Eng. At the same time in Ontario, Can., L.M. Pidgeon's process of thermally reducing magnesium oxide with silicon in externally fired retorts was introduced.

      Following the war, military applications lost prominence. Dow Chemical broadened civilian markets by developing wrought products, photoengraving technology, and surface treatment systems. Extraction remained based on electrolysis and thermal reduction. To these processes were made such refinements as the internal heating of retorts (the Magnetherm process, introduced in France in 1961), extraction from dehydrated magnesium chloride prills (introduced by the Norwegian company Norsk Hydro in 1974), and improvements in electrolytic cell technology from about 1970.

Ores and raw materials
      The eighth most abundant element in nature, magnesium constitutes 2.4 percent of the Earth's crust. Owing to its strong reactivity, it does not occur in the native state, but rather it is found in a wide variety of compounds in seawater, brines, and rocks.

      Among the ore minerals, the most common are the carbonates dolomite (a compound of magnesium and calcium carbonates, MgCO3 · CaCO3) and magnesite (magnesium carbonate, MgCO3). Less common is the hydroxide mineral brucite (Mg[OH]2) and the halide mineral carnallite (a compound of magnesium and potassium chlorides and water, MgCl2 · KCl · 6H2O).

      Magnesium chloride is recoverable from naturally occurring brines such as the Great Salt Lake (typically containing 1.1 percent by weight magnesium) and the Dead Sea (3.4 percent), but by far the largest source is the oceans (ocean) of the world. Although seawater is only approximately 0.13 percent magnesium, it represents an almost inexhaustible source.

Mining and concentrating
      Both dolomite and magnesite are mined and concentrated by conventional methods. Carnallite is dug as ore or separated from other salt compounds that are brought to the surface by solution mining. Naturally occurring magnesium-containing brines are concentrated in large ponds by solar evaporation.

Extraction and refining
      A strong chemical reagent, magnesium forms stable compounds and reacts with oxygen and chlorine in both the liquid and gaseous state. This means that extraction of the metal from raw materials is an energy-intensive process requiring well-tuned technologies. Commercial production follows two completely different methods: electrolysis of magnesium chloride or thermal reduction of magnesium oxide. Where power costs are low, electrolysis is the cheaper method—and, indeed, it accounts for approximately 75 percent of world magnesium production.

      Electrolytic processes consist of two steps: the preparation of a feedstock containing magnesium chloride and the dissociation of this compound into magnesium metal and chlorine gas in electrolytic cells.

      In industrial processes, cell feeds consist of various molten salts containing anhydrous (essentially water-free) magnesium chloride, partly dehydrated magnesium chloride, or anhydrous carnallite. In order to avoid impurities present in carnallite ores, dehydrated artificial carnallite is produced by controlled crystallization from heated magnesium- and potassium-containing solutions. Partly dehydrated magnesium chloride can be obtained by the Dow process, in which seawater is mixed in a flocculator with lightly burned reactive dolomite. An insoluble magnesium hydroxide precipitates to the bottom of a settling tank, whence it is pumped as a slurry, filtered, converted to magnesium chloride by reaction with hydrochloric acid, and dried in a series of evaporation steps to 25 percent water content. Final dehydration takes place during smelting.

      Anhydrous magnesium chloride is produced by two principal methods: dehydration of magnesium chloride brines or chlorination of magnesium oxide. In the latter method, exemplified by the IG Farben process, lightly burned dolomite is mixed with seawater in a flocculator, where magnesium hydroxide is precipitated out, filtered, and calcined to magnesium oxide. This is mixed with charcoal, formed into globules with the addition of magnesium chloride solution, and dried. The globules are charged into a chlorinator, a brick-lined shaft furnace where they are heated by carbon electrodes to approximately 1,000°–1,200° C (1,800°–2,200° F). Chlorine gas introduced through portholes in the furnace reacts with the magnesium oxide to produce molten magnesium chloride, which is tapped at intervals and sent to the electrolytic cells.

      Dehydration of magnesium brines is conducted in stages. In the Norsk Hydro process, impurities are first removed by precipitation and filtering. The purified brine, which contains approximately 8.5 percent magnesium, is concentrated by evaporation to 14 percent and converted to particulates in a prilling tower. This product is further dried to water-free particles and conveyed to the electrolytic cells.

      Electrolytic cells are essentially brick-lined vessels equipped with multiple steel cathodes and graphite anodes. These are mounted vertically through the cell hood and partially submerged in a molten salt electrolyte composed of alkaline chlorides to which the magnesium chloride produced in the processes described above is added in concentrations of 6 to 18 percent. The basic reaction is:

      Operating temperatures vary from 680° to 750° C (1,260° to 1,380° F). Power consumption is 12 to 18 kilowatt-hours per kilogram of magnesium produced. Chlorine and other gases are generated at the graphite anodes, and molten magnesium metal floats to the top of the salt bath, where it is collected. The chlorine can be reused in the dehydration process.

Thermal reduction
      In thermal production, dolomite is calcined to magnesium oxide (MgO) and lime (CaO), and these are reduced by silicon (Si), yielding magnesium gas and a slag of dicalcium silicate. The basic reaction,

      is endothermic—that is, heat must be applied to initiate and sustain it. With magnesium reaching a vapour pressure of 100 kilopascals (1 atmosphere) at 1,800° C (3,270° F), heat requirements can be quite high. In order to lower reaction temperatures, industrial processes operate under vacuum. There are three principal methods, differing by their means of supplying heat. In the Pidgeon process, ground and calcined dolomite is mixed with finely ground ferrosilicon, briquetted, and charged into cylindrical nickel-chromium-steel retorts. A number of retorts are installed horizontally in an oil- or gas-fired furnace, with their lids and attached condenser systems extending out of the furnace. After a reaction cycle at a temperature of 1,200° C (2,200° F) and under a reduced pressure of 13 pascals, magnesium crystals (called crowns) are removed from the condensers, slag is evacuated as a solid, and the retort is recharged. In the Bolzano process, dolomite-ferrosilicon briquettes are stacked on a special charge support system through which internal electric heating is conducted to the charge. A complete reaction takes 20 to 24 hours at 1,200° C below 400 pascals.

      The dicalcium silicate slag produced by the above processes has a melting point of about 2,000° C (3,600° F) and is therefore present as a solid, but, by adding alumina (aluminum oxide, Al2O3) to the charge, the melting point can be reduced to 1,550°–1,600° C (2,825°–2,900° F). This technique, utilized in the Magnetherm process, has the advantage that the liquid slag can be heated directly by electric current through a water-cooled copper electrode. The reduction reaction occurs at 1,600° C and 400–670 pascals pressure. Vaporized magnesium is condensed in a separate system attached to the reactor, and molten slag and ferrosilicon are tapped at intervals.

      After extraction by the processes described above, crude magnesium metal is transported to cast shops for removal of impurities, addition of alloying elements, and transformation into ingots, billets, and slabs. During melting and handling, molten magnesium metal and alloys are protected from burning by a layer of flux or of a gas such as sulfur hexafluoride or sulfur dioxide. For shipping and handling under severe climatic conditions, suitable ventilated plastic or paper wrappings are required to prevent corrosion.

The metal and its alloys (alloy)
      Primary magnesium is available in grades of 99.90, 99.95, and 99.98 percent, but, in practice, grades 99.95 and 99.98 have only limited use in the uranium and nuclear industries. For bulk use, grades 99.90 and 99.80 are supplied.

Metallurgical applications
      By far the greatest use of magnesium is as an alloying element in aluminum (aluminum processing). In amounts ranging from less than 1 percent to approximately 10 percent, magnesium enhances the mechanical properties as well as the corrosion resistance of aluminum alloys. Similarly, pure aluminum is used as an alloying element in many magnesium-based alloys.

      In the iron and steel industry, small quantities of magnesium are added to white cast iron to transform graphite into spherical nodules, thereby significantly improving the strength and malleability of the iron. In addition, particulate magnesium blended with lime or other fillers is injected into liquid blast-furnace iron, where it improves mechanical properties of steel by combining with sulfur and oxygen.

      Other metallurgical applications include the production of titanium, zirconium, uranium, and hafnium. By far the most important of these is in the Kroll process for reducing titanium tetrachloride to titanium metal.

Electrochemical applications
      The electronegative nature of magnesium (i.e., its readiness to give up electrons) makes it useful in dry-cell batteries and as a sacrificial anode in the cathodic protection of steel.

      Magnesium dry cells, mostly used in military and rescue equipment, combine light weight, long storage life, and high energy content. The batteries consist of a magnesium anode and a cathode of silver chloride or cuprous chloride. When activated by water, they rapidly build up voltages of 1.3 to 1.8 volts and operate at a constant potential between -55° and 95° C (-67° and 200° F).

      When magnesium comes into electrical contact with steel in the presence of water, the magnesium corrodes sacrificially, leaving the steel intact. Ship hulls, water heaters, storage tanks, bridge structures, pipelines, and a variety of other steel products are protected in this manner.

      Magnesium has been used in military pyrotechnics for many years and has found numerous uses in incendiary devices and flares. In the form of finely divided particles, it has been used as a fuel component, particularly in solid rocket propellants.

Structural applications
      The mechanical properties of magnesium improve when it is alloyed with small amounts of other metals. In most cases, the alloying elements form intermetallic compounds that permit heat treatment for enhanced mechanical properties. Magnesium alloys can be divided into two types. General-purpose alloys, suitable for applications at temperatures up to 150° C (300° F), contain 3–9 percent aluminum, 0.5–3 percent zinc, and about 0.2 percent manganese. Special alloys are used at temperatures up to approximately 250° C (480° F); these contain various amounts of zinc, zirconium, thorium, silver, and yttrium and other rare-earth metals. In addition, high-purity alloys, with low contents of iron, nickel, and copper, have greater corrosion resistance than conventional alloys.

      Magnesium is the lightest of all machinable metals. casting characteristics are excellent, since the molten metal has a low heat content and low viscosity. Magnesium alloys have limited cold-forming capabilities, owing to the hexagonal crystal structure of magnesium, but they are readily hot-worked at temperatures ranging from 150° to 400° C (300° to 750° F).

      Magnesium applications are motivated by the light weight, high strength, high damping capacity, close dimensional tolerance, and ease of fabrication of its alloys. Applications include hand tools, sporting goods, luggage frames, cameras, household appliances, business machines, and automobile parts. The aerospace industry employs magnesium alloys in the manufacture of aircraft, rockets, and space satellites. Magnesium is also used in tooling plates and, because of its rapid and controlled etching characteristics, in photoengraving.

Chemical compounds
      The compounds of magnesium form an important group of chemicals. The best-known medical compounds are milk of magnesia, or magnesium hydroxide, which is used as an antacid or as a mineral supplement to maintain the body's magnesium balance. The hydrous magnesium sulfate popularly known as Epsom salts, MgSO4 · 7H2O, is used as a laxative.

      Agricultural applications include the use of dolomite as a fertilizer in areas with acid soil and the use of magnesium oxide as a mineral addition to cattle feed at the start of the grazing season in early spring.

      The predominant industrial application of magnesium compounds is in the use of magnesite and dolomite in refractory bricks (firebrick). Bricks of high-purity magnesia are exceptionally wear- and temperature-resistant, with high heat capacity and conductivity. The more expensive fused magnesia serves as an insulating material in electrically heated stoves and ovens, while the less expensive caustic magnesia is a constituent in leaching lyes for the paper industry, where it reduces losses and allows for the processing of both coniferous and deciduous wood.

John H. Rizley Nils Høy-Petersen

Additional Reading
Comprehensive and up-to-date information on many aspects of metallurgy, individual metals, and alloys can be found in convenient reference-form arrangement in the following works: Metals Handbook, 9th ed., 17 vol. (1978–89), a massive and detailed source prepared under the direction of the American Society for Metals, with a 10th edition that began publication in 1990; Herman F. Mark et al. (eds.), Encyclopedia of Chemical Technology, 3rd ed., 31 vol. (1978–84), formerly known as Kirk-Othmer Encyclopedia of Chemical Technology, with a 4th edition begun in 1991; and its European counterpart, the first English-language edition of a monumental German work, Ullmann's Encyclopedia of Industrial Chemistry, 5th, completely rev. ed., edited by Wolfgang Gerhartz et al. (1985– ). Ed.Nils Høy-Petersen, “From Past to Future,” Light Metal Age, 48(7–8):12, 14–16 (August 1990), is a review of magnesium history. A comprehensive book on magnesium properties, alloys, and uses, with a condensed chapter on extraction technologies, is E.F. Emley, Principles of Magnesium Technology (1966). The best overview of current extraction methods is Nils Høy-Petersen et al., “Magnesium,” in Ullmann's Encyclopedia of Industrial Chemistry, 5th ed., vol. A15 (1990), pp. 559–580. Robert S. Busk, Magnesium Products Design (1987), is a thorough work on magnesium design criteria. Kh. L. Strelets, Electrolytic Production of Magnesium, trans. from Russian (1977), is a reference book on the subject.Nils Høy-Petersen

* * *

Universalium. 2010.

Look at other dictionaries:

  • magnesium — /mag nee zee euhm, zheuhm, shee euhm/, n. Chem. a light, ductile, silver white, metallic element that burns with a dazzling white light, used in lightweight alloys, flares, fireworks, in the manufacture of flashbulbs, optical mirrors, and… …   Universalium

  • Magnesium oxide wallboard — (10 mm thickness) Magnesium oxide more commonly called magnesia is a versatile mineral that when used as part of a cement mixture and cast into thin cement panels under proper curing procedures and practices can be used in residential and… …   Wikipedia

  • Magnesium/Teflon/Viton — MTV is an acronym for pyrolants based on magnesium/Teflon/Viton. Teflon and Viton are trademarks of DuPont for polytetrafluoroethylene, (C2F4) n , and vinylidenfluoride hexafluoroisopropene copolymer, (CH2CF2) n (CF(CF3)CF2) n .… …   Wikipedia

  • magnesium sulfate — noun a salt of magnesium • Hypernyms: ↑sulfate, ↑sulphate • Hyponyms: ↑Epsom salts, ↑bitter salts * * * noun : any of several sulfates of magnesium; especially …   Useful english dictionary

  • magnesium sulfate — Chem. a white, water soluble salt, MgSO4, used chiefly in medicine and in the processing of leather and textiles. Cf. Epsom salt. [1885 90] * * * …   Universalium

  • magnesium sulfate — magne′sium sul′fate n. chem. a water soluble salt, MgSO4, used in medicine and in processing leather and textiles Compare Epsom salt …   From formal English to slang

  • uranium processing — Introduction       preparation of the ore for use in various products.       Uranium (U), although very dense (19.1 grams per cubic centimetre), is a relatively weak, nonrefractory metal. Indeed, the metallic properties of uranium appear to be… …   Universalium

  • aluminum processing — Introduction       preparation of the ore for use in various products.       Aluminum, or aluminium (Al), is a silvery white metal with a melting point of 660° C (1,220° F) and a density of 2.7 grams per cubic centimetre. The most abundant… …   Universalium

  • titanium processing — Introduction       preparation of the ore for use in various products.       Titanium (Ti) is a soft, ductile, silvery gray metal with a melting point of 1,675° C (3,047° F). Owing to the formation on its surface of an oxide film that is… …   Universalium

  • nickel processing — Introduction       preparation of the metal for use in various products.       Although it is best known for its use in coinage, nickel (Ni) has become much more important for its many industrial applications, which owe their importance to a… …   Universalium

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”